Search results

Today, using lightweight structural concrete plays a major role in reducing the damage to concrete structures. On the other hand, lightweight concretes have lower compressive and flexural strengths with lower impact resistance compared to ordinary concretes. The aim of this study is to investigate the effect of simultaneous use of waste glass powder, microsilica and polypropylene fibers to make sustainable lightweight concrete that has high compressive and flexural strengths, ductility and impact resistance.

In this article, the lightweight structural concrete is studied to compensate for the lower strength of lightweight concrete. Also, considering the environmental aspects, microsilica as a partial replacement for cement, waste glass powder instead of some aggregates and polypropylene fibers are used. Microsilica was used at 8, 10 and 12 wt% of cement. Waste glass powder was added to 20, 25 and 30 wt% of aggregates, while fibers were used at 0.5, 1 and 1.5 wt% of cement.

After making the experimental specimens, compressive strength, flexural strength and impact resistance tests were performed. Ultimately, it was concluded that the best percentage of used microsilica and glass powder was equal to 10 and 25%, respectively. Furthermore, using 1.5 wt% of fibers could significantly improve the compressive and flexural strengths of lightweight concrete and increase its impact resistance at the same time. For constructing a five-story building, by replacing cement with microsilica by 10 wt%, the amount of used cement is reduced by 5 tons, consequently producing 4,752 kg less CO₂ that is a significant value for the environment.

The study provides a basis for making sustainable lightweight concrete with high strength against compressive, flexural and impact loads.

The purpose of this study is to know the influence of palm oil fuel ash and metakaolin on the strength of concrete and crack resistance of reinforced concrete beam. An ordinary portland cement has been used in the concretes production where it is an important material to be considered due to its nature that reacts with every substance present. During the cement production, a significant amount of carbon dioxide is emitted from the clinker in rotary kiln and lot of energy is required in the production processes. Such an event can be prevented by replacing the part of cement with metakaolin (MK) and palm oil fuel ash (POFA). Aside from being a cementitious alternative, the materials can also contribute to a greener environment and more sustainable building, as POFA is available in Malaysia and may be used to substitute cement and minimize pollution.

This study assesses the effect of MK and POFA on the concrete in terms of compressive strength and cracks pattern of the reinforced concrete beam based on the relevant previous studies.

From this study, the compressive strength of concrete containing MK and POFA was higher than the control mix with the percentage of improvement in the range of 0.8%–78.2% for MK and 0.5%–14%, respectively. The optimum content of MK and POFA is between the range of 10% and 15% and 10% and 20%, respectively, to achieve high strength of concrete. Other than that, the inclusion of MK to the concrete mix improves the strength of reinforced concrete beams and reduces cracks on the surface of reinforced concrete beams, whereas the inclusion of POFA to the concrete mix increases the cracks on reinforced concrete beams. The cracks appeared within the flexure zone of every beam containing the MK and POFA.

It was found that the fineness of MK and POFA has a significant influence on the mechanical properties of concrete.